Method of coating metal

ABSTRACT

A METHOD OF PROVIDING NOVEL PROTECTIVE COATING FOR METALS BY FIRING IN AN OXIDAZING ENVIRONMENT AT A TEMPERATURE IN THE GENERAL RANGE OF 1250*F. TO 1600*F., SAID COATING ESSENTIALLY CONSISTING OF ALUMINUM, A SPECIAL MILL ADDITION HAVING BOTH REFRACTORY COMPOUND AND REDUCIBLE COMPOUND CONSTITUENTS, AND A SPECIAL HOMOGENEOUS FRIT; THUS OBTAINING IMPROVED RESISTANCE OF THE METALS TO WEATHERING AND TO CORORSION BY ALKALINE OR ACID SOLUTION ATTACK UNDER ATMOSPHERIC CONDITIONS.

United States Patent 3,748,170 METHOD OF COATING METAL Harold J. Michael, Columbus, Ohio, assignor to North American Rockwell Corporation No Drawing. Original application Sept. 4, 1970, Ser. No. 69,914, now Patent No. 3,706,579. Divided and this application Sept. 1, 1971, Ser. No. 177,142

Int. Cl. B321) /00 U.S. Cl. 117-129 2 Claims ABSTRACT OF THE DISCLOSURE A method of providing novel protective coating for metals by firing in an oxidizing environment at a temperature in the general range of 1250 F. to 1600 F., said coating essentially consisting of aluminum, a special mill addition having both refractory compound and reducible compound constituents, and a special homogeneous frit; thus Obtaining improved resistance of the metals to weathering and to cororsion by alkaline or acid solution attack under atmospheric conditions.

CROSS-REFERENCES This is a divisional application of application for United States Letters Patent No. 69,914, filed Sept. 4, 1970, and now Pat. No. 3,706,579 and assigned to the assignee of this application.

SUMMARY The composition of this invention in slip form consists on a weight basis of approximately 25 to 55 parts powdered aluminum, approximately to 50 parts special homogeneous glass frit, approximately 14 to 27 parts special mill addition having both refractory compound and reducible compound constituents, approximately 0 to 10 parts flux, and water vehicle with added buffering agent; the special homogeneous glass frit has a calculated oxide content on a 100 parts weight basis consisting of to parts boric oxide, 10 to 50 parts silicon dioxide, 10 to 20 parts alkali metal oxide selected from the group consisting of the oxides of lithium, potassium, and sodium, and 10 to 40 parts of oxide selected from the group consisting of the oxides of calcium, magnesium, and zinc. Such glass frit is characterized by the fact that upon refiring to the coating firing temperature in the range of approximately 1250 F. to 1600 F., both an alkaline earth or zinc-modified boro-silicate type wetting glass system liquid phase and an alkali metal-modified bore-silicate type sealing glass system liquid phase of greater viscosity are advantageously provided in the composition. Because of the prescribed composition characteristics, the coating in slip form has a prolonged shelf life in comparison to known cermet protective coating slips.

DETAILED DESCRIPTION The following general formulation identifies the principal constituents, and preferred amounts on a 100 parts by weight basis, of the ceramic protective coating of this invention:

In addition, water, a buifering agent such as boric acid, and often a suspension control agent such as urea (such agent being in addition to any refractory such as enamelers clay or bentonite included in the composition as part of the mill addition and functioning to provide a degree of suspension control) are combined into the composition in a conventional manner to develop a slip suitable for most spray or dip coating applications. Details regarding each of the principal constituents, and particularly the required special homogeneous glass frit and the special mill addition, are provided in the further portions of the detailed description which follows.

Adjustments may be made to the composition formulation within the ranges indicated to vary the degree of resistance to weathering and cororsion attack that is obtained for metals coated by the composition. The preferred amounts given above relate to a composition that is fired to maturity at approximately 1500 and that obtains improved protection of the coated metal against attack by most acid or alkaline solutions such as are encountered under atmospheric conditions involving chemical process or combustion exhausts, salt spray environments, high-humidity concrete curing environments, and the like. In instances wherein only general resistance to weathering is required, formulation modifications may be effected through minor modification of the aluminum powder to special homogeneous glass frit constituent ratio and also by variation of the special mill addition as hereinafter described.

Aluminum powder constituent The composition of this invention utilizes atomized aluminum metal powder in the preferred amount and quantities previously indicated. The aluminum powder preferably has a maximum particle size of approximately 74 microns (200 mesh). Aluminum metal powder used in the practice of this invention and meeting the abovestated-200 mesh requirement is readily available from established commercial sources.

Special homogeneous glass frit constituent GLASS FRIT COMPOSITION Preferred Oxide Range amount,

Boric oxide 25-50 33. 5 Silicon dioxide 10-50 38. 3 Alkali metal oxide 10-20 14. 8 Alkaline earth oxide, zinc oxide 1040 13. 4

Total 100. 0

The alkali metal oxide ingredient of the homogeneous glass frit is selected from the group consisting of the oxides of lithium, potassium, and sodium with sodium oxide normally being preferred. The alkaline earth oxides are selected from the group consisting of the oxides of calcium and magnesium and may be substituted for or used instead of zinc oxide depending upon particular shelflife or corrosion resistance characteristics desired in the final coating composition. Specifically, calcium oxide and magnesium oxide are preferred as the alkaline earth oxide ingredient over zinc oxide whenever the potential alkaline or acid corrosion of the base metal is comparatively severe. Such oxides also contribute to prolonged shelflife of the composition in its slip formulation. Zinc oxide may be utilized in substitution for such alkaline earth oxides if slip shelf-life is not an important consideration and particularly if only resistance to general weathering is required. In any event, the special homogeneous glass frit of the invention develops a boro-silicate glass system for each of the Wetting and sealing phases at the composition firing temperature. The sealing phase system is an alkali metal-boro-silicate glass in each instance. The wetting phase system also is boro-silicate glass system but it has an alkaline earth oxide or zinc oxide glass network modifier depending upon the objective to be attained by the frit ingredients actually used.

EXAMPLE I Preferred Oxide Range amount Boric oxide 25-50 33. 5 Silicon dioxide. 10-50 38. 8 Calcium oxide 1040 13. 4 Sodium oxide 10-20 14. 8

Total 100.

EXAMPLE II Preferred Oxide Range amount EXAMPLE III Preferred Oxide Range amount Borio oxide 25-50 31. 0 Silicon dioxide -50 35. 0 Zine oxide 10-40 17. 0 Sodium oxide 10-20 17. 0

- Total 100.0

It should be noted that each of the above homogeneous glass frits is essentially insoluble in water. The preferred oxide compositions given in Examples I through III above may be developed by conventionally smelting the batching constituents specified in the Example IV through Example VI formulations given below, respectively:

EXAMPLE IV The batching constituents are normally dry-blended in the prescribed amounts u til thoroughly mixed and are then charged into a smelting furnace. Smelting of the batch constituents typically involves heating to a temperature in the range of from 2000 F. to 2100" F. until the glass is formed and fined. Afterwards, the fined glass is water-quenched or roller-quenched, dried, and normally powdered to a 200 mesh fineness.

As previously suggested, an important characteristic of the required homogeneous glass frit as employed in the cermet protective coating composition of this invention is that it have sufficient Wetting and seal-forming properties at the composition firing temperature. Whether adequate Wetting and seal-forming properties exist may be determined and controlled with reference to the procedure described in US. Letters Patent No. 3,203,815, issued in my name Aug. 31, 1965. With respect to the two-liquidphase glass frit of the above Example I, for instance, a sealer phase flow value of approximately 138% is obtained and also a less-viscous Wetter phase flow value of approximately 156% exists. Generally, the fusion flow values for the two different phases of the frit should have a difference in the range of 10% to 22%. Also, it is important that the glass frit constituent of the composition be essentially free of halogen elements.

Mill addition constituents The refractory and reducible compound constituents employed in the mill addition of the cermet protective coating composition of this invention are provided in the slip along with the special homogeneous glass frit to develop a substantial degree of coating thermal endurance at elevated temperatures and also to develop the required reduction reaction that occurs upon firing. The refractory compound constituent of the mill addition is normally selected from the group consisting of the oxide of aluminum, the silicates of calcium and magnesium, bentonite, and conventional enamelers clay. The reduction constituent in the mill addition is selected from the groups consisting of the oxides of cobalt, titanium, zinc, and zirconium and the sulfides of antimony and cadmium, which reduce in the presence of molten aluminum at the coating firing temperature resulting in the formation of intermetallic compounds that develop the desired corrosionresistance characteristic. It should be noted that the use of titanium dioxide as the reducible compound ingredient of the mill addition is particularly advantageous in instances where it is required that the coated metal develop improved resistance to corrosion attack by acid or alkaline solutions at essentially atmospheric conditions.

Flux constituent To the extent that use of a flux is desired to improve the bond of the cermet protective coating of this invention to the coated metal, lithium titanate is a preferred material. In the embodiment of the coating composition given in connection with Example VII below, the amount of flux utilized is 5 parts by weight of lithium titanate. In the Example VIII and Example IX cermet protective coating compositions, a flux addition has been omitted without adversely affecting resistance properties of the coated workpiece or coating relative to general weathering. Generally, no more than 10 parts by weight of flux such as lithium titanate is required for applications of the invention.

Minor composition constituents It is sometimes preferred that a conventional suspens1on control agent such as urea be utilized in the composition in addition to any enamelers clay or bentonite that is provided in the mill addition as a refractory but that also functions to control solids suspension in the slip. It further is important that boric acid or its functional equivalent be added to the water in the slip prepared for spray coating or other methods of application for purposes of buffering the mill liquor for prolonged periods such as two to three months of shelf life time. The parts Composition slip formulations A preferrer embodiment of the coating composition of this invention in a slip formulation suitable for spray coating applications is detailed immediately below as Example VII. The amounts given for the various constituents are on a parts by weight basis.

EXAMPLE VII Constituent: Preferred amount Atomized aluminum metal powder 40.0 Example I special homogeneous glass frit 40.0 Neutral enamelers clay mill addition 6.0 Bentonite mill addition 1.0 Titanium dioxide mill addition 8.0 Lithium titanate flux 5.0 Urea 0.25 Boric acid buffering agent 2.0 Tap water 50.0

The constituents listed above, excepting the aluminum metal powder and urea, ar preferably first mixed in the prescribed proportions and ball milled for one hour. The milled slip, having a specific gravity of approximately 1.5, is then adjusted in acidity-alkalinity as necessary to a pH value in the range of 7.3 to 7.8 using a saturated aqueous solution of boric acid. The aluminum metal powder and urea are next added to the slip and mixed as by blunging. The resulting slip is normally suitable for application by conventional spraying techniques although further suspension control may be eifected if necessary using sufficient electrolyte solution comprised of magnesium sulfate in tap water. As previously mentioned, the special homogeneous glass frit is usually powdered to at least a -200 mesh fineness.

The coating is fired to maturity in a conventional manner. It is necessary that the slip be dried completely after application to the metal to be protected and prior to firing and such may be accomplished by force-drying until all moisture is removed. Afterwards, the coated article is fired in an oxidizing atmosphere at 145 F. to 1500 F. to maturity which is normally attained after a minimum of ten minutes at the desired temperature depending upon the metal mass. Cooling is accomplished in a normal room atmosphere and a final fired coating thickness of 3 to 5 mils is generally sufiicient for good corrosion protection.

The coating composition derived from the principal constituents of the slip is particularly suitable for protecting metal that will possibly be subjected to corrosion by alkaline or acid solution attack under atmospheric conditions. The Example VII slip formulation also has excellent shelf life after preparation and prior to application.

The following Example VIII and Example IX slip formulations relates to variations of the coating composition of this invention that are satisfactory when general weathering is required and long slip shelf life is not necessary.

EXAMPLE VIII Constituent: Preferred amount Atomized aluminum metal powder 50.0 Example II special homogeneous glass frit 35.0 Zinc oxide mill addition 5.0 Cadmium sulfide mill addition 5 .0 Enamelers clay mill addition 5.0 Bentonite mill addition 1.0 Urea 0.5 Boric acid buffering agent 1.5 Tap water 50.0

6 EXAMPLE IX Constituent: Preferred amount Atomized aluminum metal powder 50.0 Example III special homogeneous glass frit 35.0

Zinc oxide mill addition 10.0 Cadmium sulfide mill addition 1.0 Enamelers clay mill addition 5 .0 Bentonite mill addition 1.0 Urea 0.5 Boric acid buffering agent 1.5 Tap Water 50.0

The procedure that is preferred for preparing the above coating compositions into slip form for suitable spraying is the same as that set forth in connection with the Example VII formulation. The steps of application of the resulting slip to the to-be-protected metal and firing to maturity are also essentially identical. In most instances it is preferred that the metal to be coated using the composition of this invention be cleaned prior to application of the slip formulation either by acid pickling or sand blasting in a conventional manner.

The following Example X and Example XI slip formulations relate to further variations in the coating composition of this invention. Such variations are especially advantageous in coating applications respectively wherein increased resistance to corrosion under salt-spray weathering conditions is desired and wherein improved resistance to oxidation corrosion at temperatures to approximately 1400" F. over prolonged periods is required. The Example X material also provides an excellent base for subsequently applied organic finishes utilized for efiecting decorative color variations.

EXAMPLE X Constituent: Preferred amount Atomized aluminum metal powder 35.0 Example I special homogeneous glass frit 45.0 Zirconium oxide mill addition 8.0 Magnesium silicate mill addition 5 .0 Enamelers clay mill addition 6.0 Bentonite mill addition 1.0 Urea 0.25 Boric acid buffering agent 2.0 Tap water 55.0

EXAMPLE XI Constituent: Preferred amount Atomized aluminum metal powder 50.0 Example I special homogeneous glass frit 28.0 Zirconium oxide mill addition 10.0 Cobalt oxide mill addition 5.0 Enamelers clay mill addition 6.0 Bentonite mill addition 1.0 Urea 0.25 Boric acid buffering agent 2.0 Tap water 55.0

The procedure preferred for preparing the above Example X and Example XI formulations is essentially the same as previously detailed in connection with the other example material formulations.

Panels of SAE 1010 low-carbon steel have been provided with the described protective coating composition in the manner indicated above and have been tested in both alkaline and acidic environments under room temperature conditions to establish that improved protection against corrosion attack is obtained for the base metal by practice of this invention. More specifically, SAE 1010 low-carbon steel sheet metal panels first coated with the material of Example VII as suggested and then subjected to the Gardner Impact Test at a 36 foot-pound test level, the PEI Deformation Adherence: Test using an X-configured die, and a conventional 180 conical bend test, were each afterwards additionally subjected to prolonged exposure under standard salt spray, intermittent immersion, and high alkaline environment tests. The standard salt spray test involved a sodium chloride solution and 100% humidity environment for 1500 hours; the alkaline environment test involved a similar level of humidity using an alkali hydroxide solution with a pH value of 11 to 12. The intermittent immersion test involved a 3% sodium chloride solution with the panel being subjected to minutes solution immersion each hour over a period of 1000 hours. Each of the previously deformed coated panels after the stated exposure evidenced no deterioration or attack in the underlying metal as determined by visual examination. Also, a similarly coated panel was subjected to etching by a 10% hydrochloric acid and 10% sulfuric acid solution for a total of 312 hours. The coated panel substrate evidenced a loss of thickness less than for Type 316L stainless steel subjected to the same exposure for the same period of time.

Two additional slip formulations having the composition of this invention are detailed in the following Example XII and Example XIII slips:

EXAMPLE XII Constituent: Preferred amount Atomized aluminum metal powder 35.0 Example II special homogeneous glass frit 45.0 Zirconium oxide 8.0 Magnesium silicate mill addition 5.0 Enamelers clay mill addition 6.0 Bentonite mill addition 1.0 Urea 0.25 Boric acid buffering agent 2.0 Tap water 55.0

EXAMPLE XIII Constituent: Preferred amount Atomized aluminum metal powder 40.0 Example I special homogeneous glass frit 41.0 Titanium dioxide mill addition 12.0 Enamelers clay mill addition 6.0 Urea 0.25 Bentonite mill addition 1.0 B'oric acid buffering agent 2.0

Tap water 50.0

It should be noted that the Example XII slip utilizes the homogeneous glass frit of Example II rather than the Example I frit identified in connection with the slip formulation of Example X. This particular substitution will result in a protective coating exhibiting greater resistance to weathering than the Example X formulation. The Example XIII slip formulation is similar to the composition set forth in connection with Example VII except that no fluxing agent is included.

I claim:

1. A method of providing a ferrous metallic article surface with a coating that is resistant to oxidation corrosion, comprising the steps of:

(a) applying a composition consisting essentially, on a 100 parts total weight basis, of to 55 parts by weight of powdered aluminum metal, 20 to 50 parts by weight of homogeneous solid phase glass frit, 14 to 27 parts by weight of mill addition, and water 8 and sufficient buffering agent to control slip acidityalkalinity to a pH in the range of approximately 7.3 to 7.8 on said ferrous metallic article surface, and

(b) firing said ferrous metallic article surface and said applied composition at an elevated temperature in the range of approximately 1250 F. to 1600 F. for sufi'icient time to f se said composition to said ferrous metallic article surface, said composition mill addition having 8 to 15 parts by weight of reducible compound selected from the group consisting of the oxides of cobalt, titanium, zinc, and zirconium and the sulfides of antimony and cadmium, and having 6 to 12 parts by weight of refractory compound from the group consisting of the oxide of aluminum, the silicates of calcium and magnesium, clay, and bentonite, and said homogeneous solid phase glass frit consisting at said elevated temperature of a seal-forming bore-silicate glass system liquid phase with an alkali metal glass network modifier from the group consisting of lithium, potassium, and sodium and a less viscous wetting bore-silicate glass system liquid phase with a glass network modifier from the group consisting of calcium, magnesium, and zinc.

2. An article of manufacture having a ferrous metallic surface and a ceramic and metallic protective coating fused to said surface, said coating being fused to said surface at an elevated temperature in the range of approximately 1250 F. to 1600 F. from a composition comprised of 25 to 55 parts by weight of powdered aluminum metal, 20 to 50 parts by weight of homogeneous solid phase glass frit, 14 to 27 parts by weight of mill addition, and 0 to 10 parts by weight of flux, said composition mill addition having 8 to 15 parts by weight of reducible compound selected from the group consisting of the oxides of cobalt, titanium, zinc, and zirconium and the sulfides of antimony and cadmium, and having 6 to 12 parts by weight of refractory compound from the group consisting of the oxide of aluminum, the silicates of calcium and magnesium, clay, and bentonite, and said homogeneous solid phase glass frit consisting at said elevated temperature of a seal-forming boro-silicate glass system liquid phase with an alkali metal glass network modifier from the group consisting of lithium, potassium, and sodium and a less viscous wetting bore-silicate glass system liquid phase with a glass network modifier from the group consisting of calcium, magnesium, and zinc.

References Cited UNITED STATES PATENTS 2,898,236 8/1959 Long 117--124 3,184,320 5/1965 Michael 106-48 3,203,815 8/1965 Michael l06-49 3,527,649 9/1970 Sullivan 106-48 WILLIAM D. MARTIN, Primary Examiner J. A. BELL, Assistant Examiner U.S. Cl. X.R.

mg UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION Patent No 3,748,170 Dated July 24, 1973 Inventor) Harold J. Michael It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

"Ti Column 1, line 20, change cororsion to corrosion Column 3, after line 11., add paragraph as follows: Three specific examples of the homogeneous glass frit constituent used in the practice of this invention are given in the following Examples I through III formulations:

Signed and sealed this 16th day or April 19m.

(SEAL) Attest:

EDWARD I I'.FLETCHIEIR,JR. I C MARSHALL DANN Attssting Officer Commissioner of Patents "M050 UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION Patent No. 3,748,170 Q Dated July 2 4, 1973 InventoI-(g) Harold J. Michael I It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

Column 1, line 20, change "cororsion" to corrosion Column 3, after line ll, add paragraph as follows: Three specific examples of the homogeneous glass frit constituent used in the practice of this invention are given in the following Examples I through III formulations:

Signed and sealed this 16th. day or April 19m.